Barrier effect of DLC thin films for potential application in biomedicine
Conference Proceedings, NANOCON 2015, 7th International Conference on Nanomaterials - Research & Application, October 14th – 16th 2015; TANGER Ltd., Ostrava; Brno 2015; Pages 495-499
- Druh výsledku: Článek ve sborníku (Article in the proceedings)
- Autor: Čmelík Jiří, Hájková Pavlína, Voleský Lukáš
- ISBN: 978-80-87294-63-5
- Vydáno/uděleno: 2015
Popis
The aim of the presented paper was the investigation of the barrier properties of Diamond Like Carbon (DLC) thin films used for biomedical applications. The DLC films were prepared by the Plasma Enhanced Chemical Vapour Deposition (PECVD) from methane. Stainless steel AISI type 316L was used as a substrate. Samples were placed on the excitation RF electrode. The self-bias ranged from - 700V to -800V and the deposition time varied from 1 min to 15 min. The working gas methane pressure during process was 20 Pa. Morphology of obtained DLC layers was characterized by AFM and SEM microscopy and the coating thickness by calotest method. The surface chemical composition was identified by EDS analysis. The coated samples as well as the pure substrate were tested for leaching of allergenic nickel into environment. Physiological solution was used as a model matter for this purpose. The content of nickel in the solution was monitored using ICP-OES analysis. The obtained results proved that the barrier effect was achieved even in case of 50 nm thick DLC film.